China-Lost-Wax-Stainless-Steel-Cast-Fork

Specifications:
Materials: stainless steel
Made by investment casting
Finish: polishing
Weight: 0.1~1000 gram
Design and production as per customer's requirement
We can make assembly products for you
Short delivery lead time for both samples and orders

Investment casting process describing:
We offer customers two types of investment cast processes
They are the shell(Silicasol) process and the water glass process
The shell process is used to cast complex high quality parts with requirements of a very good surface finish and close dimensional tolerances
The water glass process is typical of the process in the early stages of investment castings
It generally capable of much larger castings than the shell process, but does not have as good of surface finish or tolerances
Water glass process provides parts that have better surface finish and dimensional tolerances than sand castings
A wide range of alloys is available for both processes
They includes carbon steels, low alloy steels, stainless steels, tool steels and copper based alloys
Other material may be available upon request
Shell investment cast parts can range from a weight of just a few ounces to approximately 50 pounds
If you are concerned with precision in very small parts, we are especially proficient at very fine detail work including teeth and serrations
Water glass castings may range in weight from several ounces to approximately 175 pounds
First article layouts and spectrometer material certifications are provided with all first article samples
A variety of secondary operations can be performed on both types of investment castings
They includes heat treatment, machining, plating, painting, polishing and buffing, assembly services and even custom packaging
         Materials that can be used in our investment casting process
 
 
Carbon Steel
Standard-Spec.No.& Grade Chemical Composition≤
(%)
Mechanical Properties≥ NOTE:
(1) S,P≤0.04%
(2) C,Mn% can also be agreed upon by manufacturer and purchaser.
(3) Heat Treat: Normalize(N)+Temper(T) or Quench(Q)+T,selected by Foundry.
GB
China
JIS
Japan
ASTM
U.S.A.
C Si Mn T.S. σb
(N/mm2)
Y.S. σs
(N/mm2)
EL
δ%
R.A.
ψ%
ZG200-400 SC420 A27 60-30 0.2 0.5 0.8 400 200 25 40
ZG230-450 SC450 65-35 0.3 0.9 450 230 22 32
ZG270-500 SC480 70-40 0.4 500 270 18 25
ZG340-640 SCC3B A148 80-50 0.6 0.6 640 240 10 18
 
High Alloy Cast Steel
Standard-Spec.No Chemical Composition% Mechanical Properties≥
GB China JIS
Japan
ASTM(AISI)
U.S.A.
C Si Mn Cr Ni Others T.S.
σb
(N/mm2)
Y.S.
σs
(N/mm2)
EL
σ%
ZG1Cr13 SCSI CA-15(410) ≤0.15 ≤1.50 ≤1.00 11.5-14.0 ≤1.00 Mo≤0.05 620 450 16
ZG0Cr18Ni9 SCS13 CF8(304) ≤0.08 ≤2.00 ≤1.50 18.0-21.0 8.0-11.0
440 185 30
ZG1Cr18Ni9 SCS12 CF20(302) ≤0.20 ≤2.00 ≤1.50 18.0-21.0 8.0-11.0
480 205 28
ZG0Cr18Ni12Mo2Ti SUS316 CF-8M(316) ≤0.08 ≤1.50 ≤1.50 18.0-21.0 9.0-12.0 Mo 2.0-3.0
Ti 0.7
490 216 30
ZG0Cr17Ni4Cu4Nb SUS630 CB-7Cu ≤0.07 ≤1.00 ≤1.00 15.5-17.0 3.0-5.0 Cu 2.3-3.0
Nb 0.14-0.45
980 785 5
ZGMN13-3 SCMnH2 17-4PH 0.90-1.30 0.30-0.80 11.0-14.0

S≤0.05,
P≤0.08
686
35
ZG3Cr18Ni25Si2 SCH19 A128 B-1 0.20-0.50 ≤2.00 ≤2.00 19.0-23.0 23.0-27.0 Mo≤0.50 435 230 8
ZG4Cr25Ni20Si2 SCH22 A297 HN 0.35-0.45 ≤1.75 ≤1.50 23.0-27.0 19.0-22.0
450 240 10
Note:S,P≤0.04% except 13%Mn Steel(ZGM13-3)
 
 Copper-base Cast Alloy
Standard-Spec.No. Chemical Composition% Mechanical Properties≥
GB China JIS Japan ASTM U.S.A Sn Zn Pb Si Cu T.S.σb
(N/mm2)
Y.S.
σ%
EL HBW Hardness
ZCuSn5Pb5Zn5 BC6 C83600 4.0-6.0 4.0-6.0 4.0-6.0
Balance 200 90 13 60
ZCuSn10Zn2 BC3 C90500 9.0-11.0 1.0-3.0

240 120 12 70
ZCuZn16Si4 SZBC3 C87800
Balance
2.5-4.5 79.5-81.0 390
20 100
ZCuZn40Pb2
C85700
0.5-2.5
58.0-63.0 220 120 15 80
 