There are many factors affecting the magnetic separator. There are two main points in the following: 1. The most important factor affecting the magnetic separation effect of the magnetic separator is the feeding size of the magnetic input. The thickness of the ore-bearing grain size indicates the degree of separation of the ore monomer, that is, the degree of separation of the magnetic ore particles from the gangue particles. If the ore particle size is small, it means that the mineral monomer has high separation degree and can obtain satisfactory selection index; if the ore particle size is relatively coarse, it means that the mineral is not fully dissociated, the monomer separation degree is not high, and the opposite body is more That is, the magnetic particles and the gangue still have a considerable portion combined. Since the continuous body is also quite magnetic, the selection can be selected for a considerable portion to reduce the concentrate grade. Therefore, it is required that the minerals to be fed into the magnetic separator must sufficiently achieve monomer separation. For the ore with a coarse grain size, as long as the mineral and the gangue have reached the monomer separation, the particle size is not necessarily too fine. Such ore sometimes has a coarser grain size, but the quality of the sorting is not low. The main reason for this is that the ore is densely grained, and the useful mineral and the gangue are separated to some extent. 2. The slurry concentration is one of the main factors affecting the magnetic separation effect of the magnetic separator. It mainly refers to the overflow concentration of the classifier. If the concentration of the slurry is too large, resulting in too high a sorting concentration, the quality of the concentrate will be seriously affected. Because the concentrate particles are easily covered by finer gangue particles and the package is not separated at this time, they are selected together to lower the grade. If the concentration of the slurry is too small, the concentration will be too low, and the flow rate will increase. The selection will shorten the pairing, so that some small magnetic particles that would have been available should fall into the tailings to increase the grade of the tailings and cause losses. Therefore, the pulp concentration should be adjusted as needed. The adjustment at the magnetic separator is mainly adjusted by the size of the blown water for the mine. However, the most important thing is that the graded overflow concentration must be completed according to the magnetic separation requirements. The maximum concentration of the feed slurry should not exceed 35%, and the control is generally about 30%. It should be determined according to the actual situation.
The company produced heat - resistant steel heat treatment furnace components, products sold throughout the country. In many years of continuous development and development, innovation of a number of new materials, further to meet the heat resistant leather and deformation of the use of requirements. Components can be produced from 0.1kg to 1500kg.
Product specifications series, RX box furnace bottom plate, RJJ carburizing furnace horse boiler, charging frame, grid plate and other components from 15kw-105kw various specifications, can be supplied in a complete set.
For heat treatment multi-purpose furnace, well furnace, continuous push rod furnace
Product specifications series, RX box furnace bottom plate, RJJ carburizing furnace horse boiler, charging frame, grid plate and other components from 15kw-105kw various specifications, can be supplied in a complete set.
It is suitable for casting and welding stirring fans of various furnace types
Jiangsu Huaye Special Steel Manufacturing Co., Ltd. , https://www.huayecasting.com